Solids
1/2" to 13" OD
Tubes
1" to 16" OD
Rectangles
Up to 20"
Standard Lengths
144"
Typical Uses
Automotive
Automotive Fittings
Fasteners
Washers
Industrial
Thrust Washers, Pumps, Bushings, Machine Parts, Main Spindle Bearings, Machine Tool Bearings, Bearings for Cranes, Trunion Bearings, Roll Neck Bearings, Rolling Mill Bearing, Linkage Bushings for Presses, Fuel Pump Bushings, Water Pump Bushings, Diesel Engine Wrist Pin Bushings, Forging Press Toggle Lever Bearings, Hydraulic Press Stuffing Box, Hydraulic Press Main Lining, Pump Impellers, General Purpose Bushings, Fittings, Pump Fixtures, Insert Bearings, Bearings
Similar or equivalent specification
| CDA | ASTM | ASARCON | SAE | AMS | FEDERAL | INGOT | MILITARY | OTHER |
|---|---|---|---|---|---|---|---|---|
| C93200 | ASTM | 77 | SAE 660 | QQ-C-390 B type iii | 315 | MIL-B-11553 Comp. 12 | ||
| B505 | SAE J461 | |||||||
| SAE J462 |
Chemical Composition
| ALLOY | Cu% | Sn% | Pb% | Zn% | Fe% | Ni% | Sb% | P% | S% | AI% | Mn% | Si% |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| C93200 | 81.00- | 6.30- | 6.00- | 2.00- | 0.20 | 1.00* | 0.35 | 1.5 | 0.08 | 0.005 | N/A | 0.005 |
| 85.00 | 7.50 | 8.00 | 4.00 |
Chemical Composition according to ASTM B505-08
Note* Single values represent maximums.
*In determining copper minimum, copper may be calculated as copper plus nickel.
Machinability
| Alloy | Machinability Rating | Density (lb/cu in.) |
|---|---|---|
| C93200 | 70 | 0.322 |
Mechanical Properties
Tensile Strength, min
Yield Strength, at .5% extension under load min
Elongation in 2 in. or 50 mm min, %
Brinell Hardness, Min
Remarks
| ksi | MPa | ksi | MPa | |
|---|---|---|---|---|
| 35 | 241 | 20 | 138 | 10 |
Mechanical Properties according to ASTM B505-08
Physical Properties
| US Customary | Metric | |
|---|---|---|
| Melting Point – Liquidus | 1790 F | 977 C |
| Melting Point – Solidus | 1570 F | 854 C |
| Density | 0.322 lb/in3 @ 68 F | 8.91 gm/cm3 @ 20 C |
| Specific Gravity | 8.910 | 8.91 |
| Electrical Resistivity | 85.90 ohms-cmil/ft @ 68 F | 14.29 microhm-cm @ 20 C |
| Electrical Conductivity | 120 %IACS @ 68 F | 0.07 MegaSiemens/cm @ 20 C |
| Thermal Conductivity | 33.60 Btu- ft/(hr – ft2-oF)at 68 F | 58.2 W/m – oK at 20C |
| Coefficient of Thermal Expansion | 100 – 10-6 per oF (68-212 F) | 18.0 – 10-6 per oC (20-100 C) |
| Specific Heat Capacity | 0.090 Btu/lb/oF at 68 F | 377.1 J/kg – oK at 293 K |
| Modulas of Elasticity in Tension | 14500 ksi | 100000 MPa |
Physical Properties provided by CDA
Fabrication Practices
| Joining Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Good |
| Oxyacetylene Welding | Not Recommended |
| Gas Shielded Arc Welding | Not Recommended |
| Coated Metal Arc Welding | Not Recommended |
Thermal Properties
| Treatment | Temp./Time – US | Temp./Time – SI |
|---|---|---|
| Stress Temperature | 500 | 260 |
| Solution Minimum | ||
| Solution Maximum | ||
| Solution Time | 0.0 | |
| Solution Medium | None | |
| Precipitation Value | ||
| Precipitation Time | ||
| Precipitation Medium | None | |
| Annealing Minimum | ||
| Annealing Maximum | ||
| Annealing Time | ||
| Hot Works Minimum | ||
| Hot Works Maximum |